Petrothene GA1810 is a series of pelletized linear low density polyethylene resins selected by customers for applications that require maximum strength and toughness. These products offer excellent additive homogeneity, require no transfer equipment modification, and facilitate clean and safe handling. Typical applications include heavy duty shipping sacks, trash can liners, commercial and industrial packaging, as well as food and consumer packaging. The Petrothene GA1810 series offers enhanced film strength, drawdown, toughness and heat seal strength. In addition, these resins have excellent low temperature resistance for applications such as stretch film and frozen food packaging.
PETROTHENE LLDPE GA1810T
Request for Quotation
Min (1 piece)
PETROTHENE LLDPE GA1810T
Request for Quotation
Min (1 piece)
Per Standard Bag = 25KG
Per Standard Pallet = 55 BAG
Terms and Conditions:
1. The principle of “while stocks last” will be applied.
2. All purchases made are non-refundable.
3. Orders weighing below 1,000kgs are strictly for own collection from the seller’s warehouse.
4. Free delivery is exclusively offered within West Malaysia for orders meeting the MOQ.
5. Additional charges may be applicable for Kelantan, Terengganu, and Pahang.
Compare
SKU: GA1810T
Categories: PE, LLDPE, Request Quotation, Plastic Resins
Tags: LLDPE, Petrothene, GA1810T, Blown Film, Sheet Extrusion
Report Abuse- Description
- Shipping
- Additional information
- Discussion (0)
- Vendor Info
- More Products
- Product Knowledge
Shipping States: Penang (Pulau Pinang) (Malaysia), Perak (Malaysia), Kedah (Malaysia), Perlis (Malaysia), Negeri Sembilan (Malaysia), Malacca (Melaka) (Malaysia), Johor (Malaysia), Kuala Lumpur (Malaysia), Putrajaya (Malaysia), Selangor (Malaysia), Pahang (Malaysia), Kelantan (Malaysia), Terengganu (Malaysia)
| Weight | 25 kg |
|---|---|
| Application | Agriculture Film, Bags & Pouches, Can Liners, Film Wrap, Food Packaging Film, Heavy Duty Packaging, Lamination Film, Liner Film, Retail Carryout Bags, Shrink Film |
| Market | Flexible Packaging, Rigid Packaging |
| Processing Mehtod | Blown Film, Sheet and Profile Extrusion |
| Melt Flow Rate, (190 °C/2.16 kg) | 1.0 g/10 min (ASTM D1238) |
| Base Resin Density, (23 °C) | 0.918 g/cm³ (ASTM D792) |
| Product Density, (23 °C) | 0.923 g/cm³ (ASTM D792) |
| Dart Drop Impact Strength, F50 | 200g (ASTM D1709) |
| Tensile Strength at Break (MD/TD) | MD: 52MPa / TD: 45MPa (ASTM D882) |
| Tensile Elongation at Break (MD/TD) | MD: 620% / TD: 700% (ASTM D882) |
| 1% Secant Modulus (MD/TD) | MD: 240 MPa / TD: 290 MPa (ASTM D882) |
| Elmendorf Tear Strength (MD/TD) | MD: 400g / TD: 600g (ASTM D1922) |
| Thermal: Vicat Softening Temperature | 105°C (ASTM D1525) |
| Optical: Haze | 17% (ASTM D1003) |
| Optical: Gloss, (45°) | 45% (ASTM D2457) |
| Additive: Slip | 1000ppm (LYB Method) |
| Additive: Antiblock | 6750ppm (LYB Method) |
| Additive: Polymer Processing Aid | None (LYB Method) |
| Notes | Film sample used for testing was 1.0 mil gauge, 2.5:1 BUR. These are typical property values not to be construed as specification limits. |
| Processing Techniques | Recommended processing conditions for this product are a melt temperature of 400 – 450 °F and a 1.5 to 3.0:1 blow-up ratio. Using proper techniques, these products can readily be drawn below 0.90 mils at optimum production rates. Specific recommendations for resin type and processing conditions can only be made when the end use, required properties and fabrication equipment are known. |
Vendor Information
- Store Name: Toling Corporation (M) Sdn. Bhd.
- Vendor: Toling Corporation (M) Sdn. Bhd.
- No ratings found yet!
-
New
Lotte PP PD943 HOMO TITANPRO
Login to view price RFQ -
Lotte PP PM430 HOMO TITANPRO
Request for QuotationMin (50 piece)RFQ -
New
Lotte PP SM598 COPO TITANPRO
Login to view price RFQ -
New
Lotte PP SM398 COPO TITANPRO
Login to view price RFQ -
TOPILENE PP F501N
Request for QuotationMin (1 piece)RFQ -
TORAY Toyolac 920 555IC
Request for Quotation RFQ
Details
Plastic Number: 7Raw Material: USA
What others are saying
There are no contributions yet.